C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Ni(%) | Tensile stress (Mpa) | Elongation (%) | C(%)(%) 0.35-0.75 | Si(%)(%) ≦2.5 | 0.35-0.75 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | 0.35-0.75 | 0.35-0.75 | 0.35-0.75 | 0.35-0.75 | 0.35-0.75 |
---|
Heat Resisting Steel Castings
Steel Type | Standard | Country Code | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | SCH20 | 4002 | CNS | 0.35-0.75 | ≦2.5 | ≦2.0 | ≦0.04 | ≦0.04 | 17.0-21.0 | ≦0.5 | SCH20 | G5122 | JIS | 0.35-0.75 | ≦2.5 | ≦2.0 | ≦0.04 | ≦0.04 | 17.0-21.0 | ≦0.5 | HU | A297 | ASTM | 0.35-0.75 | ≦2.5 | ≦2.0 | ≦0.04 | ≦0.04 | 17.0-21.0 | ≦0.5 |
---|
SCH12 | SCH18 | SCH12 | SCH13 | ZG40Cr30-Ni20 | SCH11 | HK30 | SCH24 | SCH17 | SCH1 | G-X40Cr-NiSi22-9 | ZG30Cr26-Ni5 | SCH24 | HT30 | HT | SCH16 | HC | G-X40-CrSi29 | ZG35Ni24-Cr18Si2 | ZG35Ni24-Cr18Si2 |
SKT3 | FCANiSi-Cr30-5-5 | C5102W | C9200 | SUS420F | HBSC1 | 1100 | SKS51 | LY12 | CuZn36 |