DIN-GGL-NiCu-Cr15-6-2

Chemical composition

C(%) Si(%) Mn(%) Cr(%) Ni(%) Cu(%) Yield stress (Mpa) Tensile stress (Mpa) Elongation (%)
C(%)(%) ≦3.0 Si(%)(%) 1.0-2.8 ≦3.0 Cr(%)(%) 1.0-2.5 Ni(%)(%) 13.5-17.5 ≦3.0 ≦3.0 ≦3.0 ≦3.0 ≦3.0

Mechanical Properties


YieldRp0.2 (MPa) TensileRm (MPa) ImpactKV/Ku (J) ElongationA (%) Reduction in cross section on fractureZ (%) As-Heat-Treated Condition Brinell hardness (HBW)
778 (≥) 343 (≥) 22 12 32 Solution and Aging, Annealing, Ausaging, Q+T,etc 332

Applications

  • Austenitic Cast lron of Flake Graphite

Country Code

  • DIN

Standard

  • 1694


Steel Type
GGL-NiCu-Cr15-6-2

Heat treatment
Heat Treatment of steel grade GGL-NiCuCr15-6-2
Heat treated : 1498°C - 1232°C

Relate Steel Type

Steel Type Standard Country Code C(%) Si(%) Mn(%) S(%) Cr(%) Ni(%) Cu(%)
FCANiCu-Cr15-6-2 G5510 JIS ≦3.0 1.0-2.8 0.5-1.5 1.0-2.5 13.5-17.5 5.5-7.5
Type 1 A436 ASTM ≦3.0 1.0-2.8 0.5-1.5 ≦0.12 1.5-2.5 13.5-17.5 5.5-7.5
GGL-NiCu-Cr15-6-2 1694 DIN ≦3.0 1.0-2.8 0.5-1.5 1.0-2.5 13.5-17.5 5.5-7.5