JIS-FCANi-Cr30-3

Chemical composition

C(%) Si(%) Mn(%) Cr(%) Ni(%) Cu(%) Yield stress (Mpa) Tensile stress (Mpa) Elongation (%)
C(%)(%) ≦2.5 Si(%)(%) 1.0-2.0 ≦2.5 Cr(%)(%) 2.5-3.5 Ni(%)(%) 28.0-32.0 ≦2.5 ≦2.5 ≦2.5 ≦2.5 ≦2.5

Mechanical Properties


YieldRp0.2 (MPa) TensileRm (MPa) ImpactKV/Ku (J) ElongationA (%) Reduction in cross section on fractureZ (%) As-Heat-Treated Condition Brinell hardness (HBW)
648 (≥) 546 (≥) 24 14 21 Solution and Aging, Annealing, Ausaging, Q+T,etc 212

Applications

  • Austenitic Cast lron of Flake Graphite

Country Code

  • JIS

Standard

  • G5510


Steel Type
FCANi-Cr30-3

Heat treatment
Heat Treatment of steel grade FCA-NiCr30-3
Heat treated : 1594°C - 1668°C

Relate Steel Type

Steel Type Standard Country Code C(%) Si(%) Mn(%) S(%) Cr(%) Ni(%) Cu(%)
FCANi-Cr30-3 G5510 JIS ≦2.5 1.0-2.0 0.5-1.5 2.5-3.5 28.0-32.0 ≦0.5
Type3 A436 ASTM ≦2.6 1.0-2.0 0.5-1.5 ≦0.12 2.5-3.5 28.0-32.0 ≦0.5
GGL-Ni-Cr30-3 1694 DIN ≦2.5 1.0-2.0 0.5-0.8 2.5-3.5 28.0-32.0