JIS-FCANi-Cr20-3

Chemical composition

C(%) Si(%) Mn(%) Cr(%) Ni(%) Cu(%) Yield stress (Mpa) Tensile stress (Mpa) Elongation (%)
C(%)(%) ≦3.0 Si(%)(%) 1.0-2.8 ≦3.0 Cr(%)(%) 2.5-3.5 Ni(%)(%) 18.0-22.0 ≦3.0 ≦3.0 ≦3.0 ≦3.0 ≦3.0

Mechanical Properties


YieldRp0.2 (MPa) TensileRm (MPa) ImpactKV/Ku (J) ElongationA (%) Reduction in cross section on fractureZ (%) As-Heat-Treated Condition Brinell hardness (HBW)
917 (≥) 514 (≥) 12 12 31 Solution and Aging, Annealing, Ausaging, Q+T,etc 121

Applications

  • Austenitic Cast lron of Flake Graphite

Country Code

  • JIS

Standard

  • G5510


Steel Type
FCANi-Cr20-3

Heat treatment
Heat Treatment of steel grade FCA-NiCr20-3
Heat treated : 1184°C - 1848°C

Relate Steel Type

Steel Type Standard Country Code C(%) Si(%) Mn(%) S(%) Cr(%) Ni(%) Cu(%)
FCANi-Cr20-3 G5510 JIS ≦3.0 1.0-2.8 0.5-1.5 2.5-3.5 18.0-22.0 ≦0.5
Type 2b A436 ASTM ≦3.0 1.0-2.8 0.5-1.5 ≦0.12 3.0-6.0 18.0-22.0 ≦0.5
GGL-Ni-Cr20-3 1694 DIN ≦3.0 1.0-2.8 0.5-1.5 2.5-3.5 18.0-22.0 ≦0.5