Chemical composition

C(%) Si(%) Mn(%) P(%) S(%) Cr(%) Ni(%)
¨Q0.15 ¨Q1.0 ¨Q2.0 ¨Q0.045 ¨Q0.03 17.0-19.0 8.0-10.0

Applications

  • AISI 302 (1.4319, S30200) stainless steel is one kind of chrome-nickel stainless and heat-resisting steels. AISI 302 stainless steel is non-magnetic, extremely tough and ductile. Therefore, AISI 302 stainless steel is suitable in light industry, heavy industry, daily necessities and the decoration industry.

Country Code

  • AISI

Standard

  • 302


Steel Type
302

Heat treatment
AISI 302 annealing temperature is 1010-1120 degree Celsius , recommended temperature is 1400 degree Celsius
Oven stress-relief temperature and time for wire: 345 degree Celsius, 30 minutes.
Typical stress relief temperature for SS302 steel spring wire: 425-480 degree Celsius based on 30 min at temperature, only suitable for stress relief after coiling and not valid for stress relieving after shot peening. When the spring is to be used at a high temperature, the stress relief temperature should be close to the upper limit of this range to minimize relaxation in use. Otherwise, lower temperature are better.
AISI 302 typical forging temperature range is 925-1260 degree Celsius

Relate Steel Type

Steel Type Country Code C(%) Si(%) Mn(%) P(%) S(%) Cr(%) Ni(%)
302 CNS ¨Q0.15 ¨Q1.0 ¨Q2.0 ¨Q0.045 ¨Q0.03 17.0-19.0 8.0-10.0
1Cr18Ni9 GB ¨Q0.15 ¨Q1.0 ¨Q2.0 ¨Q0.035 ¨Q0.03 17.0-19.0 8.0-10.0
SUS302 JIS ¨Q0.15 ¨Q1.0 ¨Q2.0 ¨Q0.045 ¨Q0.03 17.0-19.0 8.0-10.0
302 AISI ¨Q0.15 ¨Q1.0 ¨Q2.0 ¨Q0.045 ¨Q0.03 17.0-19.0 8.0-10.0
X12Cr-Ni18-8 DIN ¨Q0.12 ¨Q1.0 ¨Q2.0 ¨Q0.045 ¨Q0.03 17.0-19.0 8.0-10.0